Solution treatment. The main purpose of water quenching after heating the steel to ~ ℃ is to dissolve the carbide in austenite and keep this state to room temperature, so that the corrosion resistance of the steel will be greatly improved. As mentioned above, in order to prevent intergranular corrosion, solid solution treatment is usually used to dissolve CrC in austenite and then cool rapidly. Air cooling can be adopted for parts, stabilization treatment and stress relief treatment.As SaltSelection process of stainless steel pipe water supply pipe.Austenitic stainless steel heat treatment austenitic stainless steel commonly used heat treatment processes are: solution treatment used for molding products. It can also be machined to harden rapidly. Good weldability. The wear resistance and fatigue strength are better than those of stainless steel.Temse,Application: utility boiler industry, mainly in key parts such as high temperature section of superheater and reheater.. It is our responsibility not to pay attention to the maintenance of the pipe during transportation, mix the pipe with corroded chemical commodities, or soak the two water into the packaging film during transportation in rainy days, which will cause rust. . It is the responsibility of the processor and manufacturer. When cutting stainless steel or iron when manufacturing goods, the scrap iron will cause rust on the surface of the steel pipe. Therefore, it is only reasonable for highly skilled technicians to deepen investigation and discussion, make a reasonable division of responsibilities, and who should be responsible for whose achievements. You can't let steel mills,Temse304 stainless steel pipe,TemseStainless steel cooling pipe, pipe factories, processors, or users bear the liability for compensation!The corrosion resistance of stainless steel depends on chromium, but because chromium is an integral part of steel, the protection is different.

The shape of pipe end stainless steel pipe can be divided into smooth pipe and threaded pipe (threaded steel pipe) according to the state of pipe end. Threading pipe can also be divided into ordinary threading pipe (pipe for conveying low pressure such as water and gas, which is connected by special thread for important threading pipe). For some special pipes, in order to make up for the impact of thread on the strength of pipe end, the pipe end is usually thickened before threading (inner thickening, outer thickening or inner and outer thickening).Cold rolled oriented silicon steel strip (sheet) represents: times of DQ + iron loss value (at the frequency of Hz, the waveform is sinusoidal, and the magnetic induction peak value is the unit weight iron loss value of T) + times of thickness value. Sometimes, reduce the proportion content of some important elements such as chromium and nickel dq represents cold rolled oriented silicon steel strip (sheet) with iron loss value of and thickness of .mm. Now the new model is q.Some reasons for product composition ratio: in order to reduce the production cost, and increase the content of other elements such as carbon. This production phenomenon that the composition ratio is not strictly in accordance with the product model and product characteristics not only greatly reduces the product quality, for example, when the chromium content of stainless steel pipe is insufficient, it not only affects the production The corrosion resistance and formability of products have potential product quality and safety hazards when they are used in chemical, equipment and production industries. At the same time, they also affect the appearance and oxidation resistance of products.Promotion,Construction materials shall be prepared and delivered to the site according to the data scheme, and shall be supplied according to the scheme.Stainless steel export is an important part of China's export economy. It plays an important role in stimulating China's economic growth. However, from the current situation of China's stainless steel foreign trade, chemical composition and application pressure, and the commodities of corresponding grades shall be selected to ensure the weld metal structure and machine function.

In engineering, the following methods are often used to prevent intergranular corrosion: reduce the amount of carbon in steel so that the amount of carbon in steel is lower than the saturated solubility of austenite in equilibrium, that is, fundamentally solve the problem of precipitation of chromium carbide (crc) on the grain boundary. Generally, the requirement of intergranular corrosion resistance can be met when the amount of carbon in steel is reduced to less than .%.quality,Hardness test: annealed stainless steel pipes with inner diameter of more than mm and wall thickness of less than mm can be tested by w-b Vickers hardness tester, which is very fast and simple, and is suitable for rapid and nondestructive qualification test of stainless steel pipes. For stainless steel pipes with inner diameter of more than mm and wall thickness of more than mm, Rockwell hardness tester shall be used to test HRC hardness. Stainless steel pipes For stainless steel pipes with inner diameter greater than mm and wall thickness less than mm, the surface Rockwell hardness tester shall be used to test HRT or hrn hardness. For stainless steel pipes with inner diameter less than mm and greater than mm, the special Rockwell hardness tester for pipes shall be used to test hrt hardness. When the inner diameter of stainless steel pipes is greater than mm, the Rockwell or surface Rockwell hardness tester can also be used to test the hardness of pipes.Stainless steel pipe appeared in Foshan, Guangdong Province in the tenth generation of the last century. With the rapid development of science and technology in recent decades, stainless steel pipe production is all over the country. Stainless steel pipe is more and more widely used. But in fact, most people, including many people in the industry,TemseDN20 stainless steel pipe, do not know much about the classification and application of stainless steel pipes. Take stainless steel pipe for example.Deburring: after the pipe is cut off the burr shall be removed to avoid cutting the sealing ring.Temse,Deformation strengthening of austenitic stainless steel stainless steel has good cold deformation performance. It can be cold drawn into very thin steel wire and cold rolled into very thin steel strip or steel pipe. After a large amount of deformation, the strength of the steel is greatly improved, especially when rolling in the subzero temperature zone. The tensile strength can reach more than MPa. This is because in addition to the cold hardening effect, there are also superimposed Deformation induced M transition.Rockwell hardness the Rockwell hardness test of stainless steel pipe is the same as Brinell hardness test. The difference is that it measures the depth of indentation. Rockwell hardness test is widely used at present, and HRC is second only to Brinell hardness Hb in steel pipe standards. Rockwell hardness can be used to measure metal materials from very soft to very hard, which makes up for the disadvantage of Brinell method, It is simpler than Brinell method and can read the hardness value directly from the dial of the hardness machine. However, due to its small indentation, the hardness value is not as accurate as Brinell method.Section shape stainless steel pipe can be divided into round pipe and special-shaped pipe according to the section shape. Special shaped tubes include rectangular tubes, rhombic tubes, elliptical tubes, hexagonal tubes, octagonal tubes and various cross-section asymmetric tubes. Special shaped pipe is widely used in various structural parts, tools and mechanical parts. Compared with circular pipe, special-shaped pipe generally has large moment of inertia and section modulus, and has large bending and torsion resistance, which can greatly reduce the structural weight and save steel.