The working principle of flat steel finishing machine in I-beam production process is to pre level and finally level the cold flat steel with two groups of leveling wheel sets staggered up and down in the thickness direction; A pair of finishing wheels arranged relatively are used to extrude the width direction so that the width is compressed to achieve the expected parameters, and the compression amount is adjustable; Straighten the width with staggered straightening wheels.The specification of I-beam is expressed in cm of waist width. For example, the waist width of No. I-beam is cm. The types of I-beam include hot-rolled ordinary I-beam Light I-beam and wide parallel leg I-beam (H-beam). The waist width of hot-rolled ordinary I-beam in China is ~ mm, expressed as No. ~ No., and the inclination of inner side wall of leg is : The pass system of rolled I-beam includes direct rolling pass system, cross rolling pass system and mixed pass system. In addition, I-beam can also adopt special rolling method.Quilali,Quilali18 how much is I-beam per meter,Galvanized pipe is a layer of galvanized ordinary steel. This is a layer and is a great anti-corrosion protection.The production process can be summarized as follows: pre leveling → finishing → straightening → post leveling. Flat steel / A / B steel with width of -, thickness of -, rectangular section and slightly pure edge. Flat steel can be finished steel, or it can be used as blank for welded pipe and thin slab for laminated thin plate.Phetchabun,At present, there is still a big gap in the production technology of C-section steel between China and foreign countries.So why is the alloy pipe easy to rust after being pickled and passivated by the software?The utility model has the advantages that the axial force of the roll is small, the axial movement is small, and the working slope is not required, and then after quenching and low-temperature tempering, pickling will be selected. Pickling of galvanized pipe is divided into chemical and electrolytic. How to prevent white rust of galvanized seamless steel pipe? It has a certain anti-corrosion effect on the pipeline.Under the action of thermal stress, because the initial temperature of the surface layer is lower than that of the heart and the shrinkage is greater than that of the heart, the heart is pulled. At the end of cooling, because the final cooling volume shrinkage of the heart cannot be carried out freely, the surface layer is compressed and the heart is pulled. That is, under the action of thermal stress, the surface of the workpiece is finally compressed and the center is pulled. This phenomenon is affected by factors such as cooling rate, material composition and heat treatment process. The faster the cooling rate, the higher the carbon content and alloy composition, the greater the uneven plastic deformation caused by thermal stress during cooling, and the greater the final residual stress. On the other hand, due to the change of microstructure during heat treatment, i.e. the transformation from austenite to martensite, the increase of specific volume will be accompanied by the expansion of workpiece volume, and each part of workpiece will undergo phase transformation successively, resulting in inconsistent volume growth and structural stress. The final result of the change of tissue stress is the tensile stress on the surface and the compressive stress in the center, which is just opposite to the thermal stress. The microstructure stress is related to the cooling rate, shape and chemical composition of the workpiece in the martensitic transformation zone.technological innovation,QuilaliHow many 20 rebar in a bundle, the thick steel plate has uniform deformation, small internal stress and no scratch on the surface. The alloy pipe produced and processed has higher coordination ability in the scope of size, specification and model of diameter and wall thickness, which has incomparable advantages of other processing technologies especially medium diameter small thick wall pipe,QuilaliQ345 seamless pipe price, and can meet a large number of customer regulations on the specification and model of alloy pipe.After isothermal quenching treatment, the modified LNs steel of case hardening steel also has the surface compressive stress characteristics obtained by heat treatment.In order to make the steel pipe workpiece have the required mechanical, physical and chemical properties, in addition to the reasonable selection of materials and forming processes, heat treatment process is often essential. Steel is the most widely used material in the mechanical industry. The microstructure of steel is complex and can be controlled by heat treatment. Therefore, the heat treatment of steel is the main content of metal heat treatment. In addition, aluminum, copper, magnesium titanium and their alloys can also change their mechanical, physical and chemical properties through heat treatment to obtain different service properties.

The flange of H-beam is of equal thickness, including rolling section and combined section composed of three plates welded. All I-beams are rolled sections. Due to poor production technology, the inner edge of the flange has a slope of : The rolling of H-beam is different from that of ordinary I-beam. Only one set of horizontal rolls is used. Because its flange is wide and has no inclination (or the inclination is very small), a group of vertical rolls must be added for rolling at the same time. Therefore, its rolling process and equipment are more complex than ordinary rolling mills. The maximum height of rolled H-section steel that can be produced in China is mm, which exceeds the welded composite section.project,Patented manufacturing process of I-beam: I-beam has become a new industrial standard for wear-resistant materials Spiral welded steel pipe (sy- for pile is made of hot-rolled steel strip coil as pipe blank, often warm spiral forming, double-sided submerged arc welding or high-frequency welding. It is used for foundation pile of civil building structure, wharf, bridge, etc.Determined by the shape, the section modulus, moment of inertia and corresponding strength of I-beam are obviously better than those of ordinary I-beam with the same single weight. When used in metal structures with different requirements, it shows its superior performance in bearing bending moment, pressure load and eccentric load. Compared with ordinary I-beam, it can greatly improve the bearing capacity and save metal by % ~ %.Quilali,Whether I-section steel is ordinary or light, because the section size is relatively high and narrow, the moment of inertia of the two main axes of the section is quite different, so it can only be directly used for members bent in the plane of their web or form lattice stressed members. It is not suitable for axial compression members or members with bending perpendicular to the web plane, which makes it very limited in the scope of application. I-beam is widely used in buildings or other metal structures. The small length of repair welding is mm; The raw material shall not exceed mm after grinding by welding edge.I-beam has wide flange, thin web, it is easy to assemble and combine into various components, which can save about % of the welding and riveting workload, greatly accelerate the construction speed of the project and shorten the construction period.