When hoisting stainless steel pipes, public slings, such as hoisting belt and public collet number, it shall prevent scratching caused by impact and collision. If there are surface scratches, electric arc traces and surface purification in the process of transportation, storage and processing, it must be completely cleaned, polished with an angle grinder, and then polished Polishing with optical sheet or metallographic sandpaper.The intergranular corrosion of austenitic stainless steel can be prevented by adding Ti, Nb and other elements that can form stable carbides (tic or NBC) and avoiding the precipitation of crc on the grain boundary.Dessalines,Allowable depth of straight track: hot rolled and hot-rolled steel pipes with diameter less than or equal to mm shall not be greater than % of the nominal wall thickness, and the large depth shall not be greater than .mm; cold drawn (rolled) steel pipes shall not be greater than % of the nominal wall thickness, and the large depth shall not be greater than .mm.The bright nickel layer on the stainless steel pipe is a silver white metal with slight yellow light. Its hardness is higher than that of copper, zinc, tin, cadmium, but lower than that of chromium and rhodium. Bright nickel has high chemical stability in air and good stability to alkali. Using Brightener on stainless steel pipe, bright nickel can be directly plated without polishing, so as to improve the hardness, wear resistance and leveling of the surface, make the appearance of stainless steel pipe consistent with other nickel plated parts, and avoid the corrosion of potential difference between stainless steel pipe and other bright nickel. After using bright nickel solution for a period of time, due to the of brightenerHollola,Decorative stainless steel pipe: usually the outer wall is relatively bright, so its name is considered. Decorative stainless steel pipe is used for decorative purposes. The stainless steel pipe for general decorative purposes is relatively thin. Because it is different from the manufacturing process of stainless steel product pipe, the price also varies greatly. The general production process of decorative stainless steel pipe is ordinary welded stainless steel pipe. Guangdong stainless steel product pipe stainless steel product pipe: generally, the surface of stainless steel product pipe is also a bright surface, and a small number of pipes with acid pickling industrial surface. As mentioned above, because the outer diameter size, mechanical properties, acid, alkali and corrosion resistance of stainless steel pipe are relatively good, Therefore, stainless steel pipes are generally used as anti-corrosion materials or hardware products in large-scale production enterprises. The production process of stainless steel pipes is one-time forming, and nitrogen protection is also added during welding.Duplex stainless steel product description: This stainless steel has good corrosion resistance in urea carbamate solution and high stress corrosion cracking resistance in chloride environment. At the same time, the duplex stainless steel has excellent mechanical properties and can be used in plant construction with high safety requirements.Since the beginning of last year, foreign countries have frequently carried out & ldquo; Double inverse & rdquo; This has a great impact on China's stainless steel casting industry. Export is a large part of the development of China's stainless steel industry and occupies a huge market share in its industrial development. In the face of economic downturn and slow development, the development of China's stainless steel industry should constantly improve product quality, Better develop overseas trade and deal with trade protectionism, combine products with environmental protection energy resources and cultural environment, and improve the competitiveness of stainless steel products. Only in this way can we achieve an invincible position in foreign trade.

Stainless steel pipe factory stainless steel products are widely used in hardware products, furniture, mechanical structure, mechanical accessories, precision medical instruments, fluid transmission pipelines, such as furniture, machinery, medical oil, natural gas, water, gas, steam and other industries.The stainless steel strip is supplied in coils, also known as strip steel. It is divided into hot rolling and cold rolling, as well as ordinary steel strip and high-quality steel strip. There are many kinds of stainless steel belts! Wide use! There are: stainless steel belt, stainless steel belt, stainless steel belt, stainless steel belt, stainless steel belt stainless steel belt, stainless steel belt, J stainless steel belt, S stainless steel belt, L stainless steel belt L stainless steel belt,DessalinesWelding method of stainless steel pipe, S stainless steel belt, stainless steel iron belt, etc! Thickness: .mm-mm, width: mm-mm, can be customized without standard!Model & mdash; The corrosion resistance is the same, and the strength is better because the carbon content is relatively high.how,Austenitic stainless steel is generally used for manufacturing and manufacturing chemical equipment components low-temperature equipment components in refrigeration industry, and can be used as stainless steel spring and clock spring after deformation strengthening.Several kinds of stainless steel backing welding used for stainless steel backing welding usually adopt TIG process. According to the actual situation of the site, professional L stainless steel pipe, s stainless steel pipe, L stainless steel pipe and other special products, old brands, the content of impurities such as P, Sb,DessalinesWest Tiecheng stainless steel strap, Bi and as should be reduced as much as possible. In addition, A-F dual phase steel can be selected, which does not correspond to stress corrosion in Cl - and oh - media. The initial micro crack will not continue to expand after encountering ferrite phase, and the ferrite content should be about % .

Using CrO and hsoho as the main components and adding an appropriate amount of mnso.ho coloring solution, the chemical coloring of stainless steel industrial pipe was carried out. The effects of pretreatment process, coloring solution temperature, mass concentration and coloring time on the color film of stainless steel industrial pipe were discussed. Through a large number of experiments, a good formula and process range of coloring solution are obtained. With the increase of temperature and time, the film thickness increases, and the color changes are brown, blue, gold, purplish red and green. After curing and sealing treatment, the colored film of stainless steel industrial pipe has more uniform surface color good reproducibility, the responsibility of the calender is that the annealed steel strip is blackened, the furnace liner is perforated, and ammonia leakage will cause rust. . The responsibility of the steel plant is that the peeling and trachoma of the steel strip will cause rust. Substandard materials will cause rust. the responsibility of the calender is that the annealed steel strip is blackened, the furnace liner is perforated, and ammonia leakage will cause rust. . The responsibility of the pipe manufacturer: the welds in the pipe manufacturer are polished rough, which will cause rust.The Chinese brand of stainless steel plate is crnimoti (CrNiMoTi with paper should also be this brand). The new brand is crnimoti stainless steel plate. The stainless steel plate is added with Ti in SUS steel to improve the intergranular corrosion resistance. It is applied to the equipment of, phosphoric acid acetic acid and acetic acid.Model & mdash; Martensite (high strength chromium steel), Series & mdash; Martensitic precipitation hardening stainless steel.The continuous casting of stainless steel pipe fittings is generally matched with the refining furnace, which has strict requirements on the chemical composition and temperature of molten steel; In order to prevent secondary oxidation of molten steel,DessalinesStainless steel seamless coil, non oxidation protection pouring is required during continuous casting production; Strict requirements for refractory materials such as ladle, tundish, nozzle and submerged nozzle.At present, stainless steel backing is divided into two processes: back argon filling and non argon filling. Back argon filling protection can be divided into solid wire + TIG process and solid wire + TIG + water-soluble paper process; The back non argon filling protection is also divided into flux cored wire backing welding and welding rod (flux coated wire) backing TIG welding.